6A02 aluminum bar is a widely used forged aluminum with medium strength (lower than other forged aluminum), poor plasticity and machinability in the annealed state, good plasticity and machinability after quenching and natural aging, and good corrosion resistance as 2A21 and 2A02 , After artificial aging, it has a tendency of intergranular corrosion. When the copper content of 6A02 aluminum bar is <0.1%, the corrosion resistance is high. 6A02 aluminum bar is easy to spot welding and hydrogen atom welding, and gas welding is still good. High plasticity in hot state, easy forging and stamping.
6A02 aluminum bar is a widely used forged aluminum with medium strength (lower than other forged aluminum), poor plasticity and machinability in the annealed state, good plasticity and machinability after quenching and natural aging, and good corrosion resistance as 2A21 and 2A02 , After artificial aging, it has a tendency of intergranular corrosion. When the copper content of 6A02 aluminum bar is <0.1%, the corrosion resistance is high. 6A02 aluminum bar is easy to spot welding and hydrogen atom welding, and gas welding is still good. High plasticity in hot state, easy forging and stamping.
Product Name | 6A02 aluminum bar |
Type | Heavy gauge foil, Medium gauge foil, Light gauge foil |
Alloy Type | 1100,1145,1050,1060,1235,3003,5052,5A02,8006,8011,8079 |
Thickness | 0.004MM-0.2MM |
Width | 3MM -500MM |
Temper | 0,T3,T4,T351,H112 |
Length | to clients’ requirement |
Surface Treatment | Mill finish/Coated/Printed/Embossed |
Standard | JIS, AISI, ASTM, GB, DIN, EN |
Packaging | Standard export packing or following customer’s demand |
Application | Flexible Pack, Food pack, Beverage industry, Construction industry |
Delivery | In general, within 8-20 working days after receiving deposit or According to Final order quantity |
6A02 aluminum bar chemical composition:
Aluminum Al: Balance Silicon Si: 0.50~1.2 Copper Cu: 0.20~0.6 Magnesium Mg: 0.45~0.9 Zinc Zn: ≤0.20 Manganese Mn: 0.15~0.35 or Cr: 0.15~0.35 Titanium Ti: ≤0.15 Iron Fe: 0.000~ 0.500 Note: Single: ≤0.05; Total: ≤0.10
6A02 aluminum bar mechanical properties:
Tensile strength σb (MPa): ≥295 Elongation δ5 (%): ≥12
Note: Longitudinal mechanical properties of bar at room temperature
Automatic cutting machine cutting,no burr on the edge corrosion resistance,good mechanical properties,oxidation resistance and not easy to rust
Automatic cutting machine cutting,no burr on the edge corrosion resistance,good mechanical properties,oxidation resistance and not easy to rust
Automatic cutting machine cutting,no burr on the edge corrosion resistance,good mechanical properties,oxidation resistance and not easy to rust